Poli(akrilamid-maleik asit) temelli hidrojel kompozitlerin hazırlanması ve karakterizasyonu

Preparation and characterization of poly(acrylamide/maleic acid)-based hydrogels composites

Abstract

The principle aim of this investigation was the preparation and characterization of the composites formed from Bentonite (B) and Zeolite (Z) minerals, and polyacrylamide-co-maleic acid (PAA-MA) hydrogel polymers. The procedures used in obtaining the polymers were also applied in preparation of the composites by direct polymerization of the monomers of interests dissolved in the suspension of B or Z. The prepared PAA-MA and the composites were characterized with the data and analysis results obtained from FT-IR, TGA, SEM, BET-porosity and Zero Point of Surface Charge (PZC). The results of FT-IR, TGA, SEM, BET-porosity and PZC analysis presented certain evidences for the formation of composites, it was impressed that the composites were the mixtures composed of two phases composing of organic (PAA-MA) and inorganic (B or Z) phases rather than the formation of polymer/mineral hybrid.

Özet

Bu araştırmanın temel amacı Bentonit (B) ve Zeolit (Z) minerallerinin hidrojel polimer olan Poliakrilamid-ko-maleik asit (PAA-MA) ile oluşturduğu kompozitini hazırlamak ve karakterize etmektir. Polimerlerin elde edilmesinde kullanılan yöntem, kompozitlerin hazırlanmasında da kullanılmış ve B veya Z içeren süspansiyon ortamında bulunan ilgili monomerlere doğrudan polimerleştirme işlemi uygulanmıştır. Hazırlanan PAA-MA ve kompozitlerin yapısal karakterizasyonunda FT-IR, TGA, SEM, BET-Gözeneklilik ve sıfır yüzey yük noktası (PZC) ile ilgili veri ve analiz sonuçları kullanılmıştır. FT-IR, XRD, TGA, SEM, BET-gözeneklilik ve PZC analiz sonuçları kompozit oluşumu ile ilgili kesin kanıtlar sunmuş, yapıların polimer/mineral hibrit oluşumundan çok biri organik (PAA-MA) ve diğeri inorganik özellikteki (B veya Z) iki faz içeren bir karışım olduğu kanısına varılmıştır.