Investigation of the Potential of Pileki Stone (İyidere, Rize) for Geopolymer Cement Production
- Pages
- 388–392
- DOI
- —
Abstract
The results of this study are based on experiments on geopolymer cement based Pileki Stone which gives local reserve in Rize and its surroundings. The effects of Na2SiO3/NaOH ratio, raw material / activator ratio, curing temperature and curing time on compressive strength were investigated in order to observe the potential production of Pileki Stone-based geopolymer cement. According to the results of the strength analysis, it is possible to produce the Pileki Stone-based geopolymer cement. Na2SiO3 / NaOH ratio 2 and raw material / activator ratio of 1.75 in 28 days at 70 ° C dry cure mixture gives the highest compressive strength value. In case of early resistance, it is recommended to cure at high temperatures and to keep the Na2SiO3 / NaOH ratio high. In addition, as the curing time increased, the compressive strength values of Pileki Stone-based geopolymers were decreased.
Özet
Bu çalışmanın sonuçları Rize ve çevresinde yöresel olarak rezerv veren Pileki Taşı esaslı geopolimer üzerinde yapılan deneylere dayanmaktadır. Pileki Taşı kullanılarak geopolimer üretim potansiyelinin araştırılması amacıyla Na2SiO3/NaOH oranı, hammadde/aktivatör oranı, kür sıcaklığı ve kür süresi gibi parametrelerin basınç dayanım üzerindeki etkileri incelenmiştir. Yapılan dayanım analizi sonuçlarına göre Pileki Taşı esaslı geopolimerin üretim potansiyeli bulunmaktadır. Na2SiO3/NaOH oranı 2 ve hammadde/aktivatör oranı 1.75 olan 28 günde 70°C sıcaklıkta kuru kür yapılan karışım en yüksek basınç dayanım değerini vermektedir. Erken dayanım söz konusu olduğunda ise yüksek sıcaklıklarda kür yapılması ve Na2SiO3/NaOH oranının yüksek tutulması önerilmektedir. Ayrıca kür süresi arttıkça Pileki Taşı esaslı geopolimerlerin basınç dayanım değerlerinde düşüş tespit edilmiştir.