The effect of various metal surface pretreatments on wettability of the base metal alloy surfaces

Ni-Cr Soy olmayan metal alaşımı yüzeyine uygulanan çeşitli aşındırma ve kum banyosu işlemlerinin metalin ıslanabilirliğine etkisi

Abstract

The base metal alloys are commonly used in ceramometal restorations. In this study the effect of various metal surface pretreatments on the wettability of the base metal alloy surfaces was compared. A total of 64 samples were prepared in 8 groups, each group corresponding to diffeent abrasives and sandblasting applications with different shapes. 50 $mu$m $AL_{2}O_{3}$ sandblasted group which surfaces weregrinded with steel fissure bur and tungsten carbide bur showed the minimum average contact angle degree values. According to the results of variance analysis (ANOVA), ceramic stone, carborundum stone, steel bur and tungsten-carbide bur used as abrasives and $AL_{2}O_{3}$ sandblasting applications at 50 $mu$m 250 $mu$m shapes had the same effect on the wettability of metal, there was no significant diffe-rence between these materials.

Özet

Son yıllarda sıklıkla kullanılır hale gelen soy olmayan metal alaşımı yüzeylerine çeşitli aşındırıcı materyaller ve farklı boyutlardaki pürüzlendirici kum banyosu uygulamasının metalin ıslanabilirliğine etkisini temas açısı (G) değerlerini ölçerek inceledik. Farklı aşındırıcı ve farklı boyuttaki kum banyosu uygulamalarına göre 8 grupta toplam 64 örnek hazırlandı. Çelik fissür frez ve tungsten karbid frezlerle 50 $mu$m'lik $AL_{2}O_{3}$ kum banyosu uygulanan gruplar ortalama en düşük temas açısı değerlerini gösterdi. Yapılan varyans analizi (ANOVA) sonuçlarına göre aşındırıcı olarak kullanılan seramik, taş, karborundum taş, çelik fissür frez ve tungsten kardib frezle, pürüzlendirici olarak 50 $mu$m ve 250 $mu$m boyutlarındaki $AL_{2}O_{3}$ kum banyosu uygulamalarının metalin ıslanabilirliğine aynı etkiyi gösterdikleri, aralarında anlamlı farka rastlanmadığı sonucuna varıldı.