Effect of silica fume on mechanic crack formations in concrete

Abstract

High strength concrete are obtained by adding the silica fume, which is an Electrometallurgy Facility’s, into concrete production. In this study, increasing on strength and mechanic crack formations of concrete, which were produced by CEM II/A-M 32.5 cement, using silica fume and superplasticizer, were investigated in the respect of microstructure. Photo of microstructure has been taken and chemical analysis has been determined by using Electron Microscope. As a result of studies, investigated micrographs and chemical analysis, silica fume; provides compactness at micro-level in concrete, occurs a regular mortar microstructure around the coarse aggregate because silica fume reactions with CH and occurs CSH, and produces positive effect in micro structure in addition to the contribution to adherence of interfacial zone.

Özet

Elektrometalurji fabrikalarının atığı olan silis dumanının betona katılmasıyla yüksek dayanımlı betonlar elde edilebilmektedir. Bu çalışmada CEM II/A-M 32.5 çimentosu, silis dumanı ve süperakışkanlaştırıcı kullanılarak üretilen betonların dayanımda meydana getirdiği artış ve mekanik çatlak oluşumları mikroyapısal olarak incelenmiştir. Elektron Mikroskobu kullanılarak mikroyapı fotoğrafları çekilmiş, kimyasal analizleri yapılmıştır. Yapılan çalışmanın sonucunda; silis dumanının betonda mikro düzeyde doluluk sağladığı, CH bağlayarak CSH’ları oluşturması nedeni ile iri agregaların etrafında düzenli bir harç yapısının oluşması, ara yüzeylerde aderansın sağlanması gibi mikroyapıda olumlu etkileri görülmüştür