The Annealing of Corundum (Ruby) in Nitrogen (N2) Air

Abstract

Abstract: Every ruby produced in the world is in different qualities with its unique characteristics. Thedevelopment of ruby’s color is effective in annealing in different atmospheres. In our work, crystal parameters,spectroscopic properties and color changes were determined by heat-treating the newly discovered ruby in thenitrogen atmosphere in Turkey. The annealing result in the nitrogen atmosphere was: a-axis 0.17% and c-axis0.25%, for R-3c: R-3c: R a-axis 7.06%, alpha angle 5.19% and a- 0.99, c-axis increased by 0.94%. Afterannealing, a large absorption peak was observed at a wavelength of 500 nm in the UV-Vis spectrometer. The redcolor of the ruby was white-light-pink after annealing. Heat treatment in the nitrogen environment caused achange in the color of the ruby.

Özet

Öz : Dünyada üretilen her yakut kendine özgü özellikleriyle farklı kalitelerdedir. Yakutun renginin geliştirilmesinde farklı atmosferlerde tavlama etkili olabilmektedir. Çalışmada, Türkiye’de yeni keşfedilen yakutun azot atmosferinde ısıl işleme tutularak, kristal parametreleri, spektroskopik özellikleri ve renk değişimleri belirlenmiştir. Azotlu atmosferde tavlama sonucu, yakutun kristal parametreleri a-ekseni % 0,88 ve c-ekseni % 0,18 oranında büyümüştür. Tavlama sonrası, UV-Vis spektrometrede 500 nm dalgaboyunda geniş absorbsiyon piki kaybolmuştur. Yakutun kırmızı rengi, tavlama sonrası beyazımsıaçık pembe renk olmuştur.