Optoelectronic Characterization of PCDTBT:PCBM Based Organic Schottky Diodes and Heterojunction Solar Cells
- Pages
- 1644–1657
- DOI
- —
Abstract
In this study, Silver/n-type Silicon/poly[N-9′-heptadecanyl-2,7–carbazole–alt-5,5-(4′,7′-di–2–thienyl-2′,1′,3′-benzothiadiazole:[6,6]-phenyl-C61-butyric acid methyl ester/Gold (Ag /n-Si/ PCDTBT: PCBM/Au) organic metal-polymer semiconductor Schottky barrier diodes were produced using 20% PCDTBT and 80% PCBM mixture as polymer interface. The current-voltage measurements of the produced diodes in the 240 - 350 K temperature range and the diode ideality factor values at these temperatures were observed to vary non-linearly, depending on the temperature in the range of 1.80 and 2.26. In the second phase of the study, Indium Tin Okside/PCDTBT:PCBM/Silver (ITO/PCDTBT:PCBM/Ag) organic solar cells were produced with 20%: 80% PCDTBT: PCBM volumetric ratio, and the characteristics of the produced solar cell was investigated. As a result of the investigation, it was observed that the power conversion efficiency of the produced solar cell was found to be 0.85%.
Özet
Bu çalışmada Gümüş/n-tipi Silisyum/poly[N-9′-heptadecanyl-2,7–carbazole–alt-5,5-(4′,7′-di–2–thienyl-2′,1′,3′-benzothiadiazole:[6,6]-phenyl-C61-butyric acid methyl ester/Altın (Ag/n-Si/PCDTBT:PC61BM/Au) organik metal-polimer yarıiletken Schottky bariyer diyotları, polimer arayüz olarak %20 PCDTBT ve %80 PCBM karışımı kullanılarak üretilmiştir. Üretilen diyotların 240 - 350 K sıcaklık aralığında akım-voltaj ölçümleri yapılarak, bu sıcaklıklardaki diyot idealite faktörü değerlerinin 1,80 ve 2,26 aralığında değiştiği gözlemlenmiştir. Çalışmanın ikinci aşamasında, İndiyum Kalay Oksit/PCDTBT:PCBM/Gümüş (ITO/PCDTBT:PCBM/Ag) organik güneş hücresi %20:%80 PCDTBT:PCBM hacimsel oranına sahip olacak şekilde üretilmiş ve güç dönüştürme verimi % 0,85 olarak bulunmuştur.