Comparison of The Effects on The Mechanical Properties of SiC, B 4 C and TiB 2 Reinforcing Elements in Aluminum 7075 Matrix Composites

Alüminyum 7075 Matrisli Kompozitlerde SiC, B 4 C Ve TiB 2 Takviye Elemanlarının Mekanik Özelliklere Etkilerinin Karşılaştırılması

Abstract

In this study, SiC, B 4 C and TiB 2 reinforcement elements were separately added to Al 7075 matrix material by powder metallurgy method. SiC, B 4 C and TiB 2 reinforcement weight ratios were applied as 5%, 10% and 20%..Measurements and experiments have been carried out to determine the mechanical properties of composites such as density, hardness, transverse rupture and wear. Microstructures of all samples were visualized with an optical microscope. According to the results, the highest hardness values (72.14 HBW) were measured in TiB 2 reinforced composites while the highest density (94.5%) and fracture strength (1418N) and the lowest wear amount (0,164 g) occurred in SiC reinforced composites. The most important factors affecting the mechanical properties have been assessed as the reinforcing phases, with increasing amounts of pores due to the increase in reinforcement ratios.

Özet

Bu çalışmada toz metalurjisi yöntemi kullanılarak Al 7075 matris malzemesi içerisine SiC, B 4 C ve TiB 2 takviyeelemanları ayrı ayrı ilave edilmiştir. SiC, B 4 C ve TiB2 takviye ağırlık oranları %5, %10 ve %20 olarakuygulanmıştır. Kompozitlerin yoğunluk, sertlik, çapraz kırılma ve aşınma gibi mekanik özellikleri belirlemekiçin ölçüm ve deneyler yapılmıştır. Tüm numunelerin mikroyapıları optik mikroskop ile görüntülenmiştir. Eldeedilen sonuçlara göre, en yüksek yoğunluk(%94,5) ve kırılma dayanımı (1418 N) ile en düşük aşınmamiktarı(0,164 g) SiC takviyeli kompozitlerde meydana gelirken en yüksek sertlik değerleri(72,14 HBW) TiB 2takviyeli kompozitlerde ölçülmüştür. Mekanik özellikleri etkileyen en önemli faktörlerin, takviye oranlarınınartışına bağlı olarak artan gözenek miktarları olduğu değerlendirilmiştir.