Magnezyum sülfat çözeltisinin buğday sapı külü katkılı ve katkısız harçlara etkisi

Abstract

In this study, an investigation was carried out on the effect of magnesium sulfate on the sulfate resistance of mortars. Experiments were carried out on the RILEM portland cement standard mortars and cement - wheat stalks ash mortars the ash was replaced % 9, 16 % and % 24 of the cement by mass. Sulfate $SO_4^{2-}$ concentrati¬ons were 10000 mg/L and 40000 mg/L. Sulfate exposures of mortars were initiated after 28 days of lime saturated water curing. Tensile strength, compressive strength and density were determined at the beginning of exposure and at the 28th, 56th, 90th and 180th days. The solutions were renewed and mass changes were measured in pe¬riods of 14 days. The effects of magnesium sulfate solutions on the properties of mortars were related by depen¬ding on the ash ratio. Ash replacement caused significant increase in sulfate resistance of mortar even at the hig¬hest sulfate concentration up to 180 days of exposure.

Özet

Bu çalışmada buğday sapı külünün, harçların sülfata karşı dayanıklılığına etkisi araştırılmıştır. Sülfat etkisini belirlemek için, $SO_4^{2-}$ konsantrasyonu 10000 mg/L ve 40000 mg/L olan magnezyum sülfat çözeltileri kullanılmıştır. Deneyler standart harçlarda ve çimento ağırlığının, % 8, % 16 ve % 24 oranlarında ikameli olarak buğday sapı külü katılmış harçlarda yapılmıştır. Numuneler 28 gün kirece doygun suda saklanmış ve 28. gün başlangıç kabul edilmiştir. Başlangıçta, 28., 56., 90. ve 180. günlerde numunelerde eğilme dayanımı, basınç dayanımı ve birim ağırlık belirlenmiştir. Çözeltiler 14 gün ara ile yenilenmiş, günerde ağırlıklar ölçülmüştür. Magnezyum sülfat çözeltilerinin harç özelliklerine etkileri kül oranına göre değerlendirilmiştir. Çimentoya kül katılması, 180. güne kadar yüksek konsantrasyonda bile harcın karşı dayanıklılığına olumlu etki yapmıştır.