Effects of chemical composition and water-cement ratio on sulfate resistance of mortars

Çimento kompozisyonu ve su-çimento oranının harçların sülfat direncine etkileri

Abstract

This paper presents an investigation on the sulfate resistance of ordinary Portland cement (CEM I), sulfate resistant Portland cement and blended cements containing different amounts of natural pozzolan and/or low-lime fly ash. The performance of cements was observed by exposing the prepared mortar specimens to a 5% Na2SO4 solution for 26 weeks. It was concluded that the cement chemistry and water-cement ratio (w/c) of mortars were the two parameters affecting the performance of mortars against an attack. Asa result of this experimental study it was found out that the effect of w/c was more important for low sulfate resistant cements with higher$C_3A$ amounts when compared to high sulfate resistant cements with lower $C_3A$ amounts.

Özet

Bu makale, farklı yüzdelerde uçucu kül ve tras içeren katkılı çimentoların, CEM I-Portland çimentosu ve sülfata dayanıklı çimentoya göre sülfat etkisine karşı gösterdikleri performanslarını karşılaştıran bir deneysel çalışmayı sunmaktadır. Bu kapsamda, yedi farklı çimento ile farklı su-çimento (S/Ç) oranlarında harç karışımları hazırlanmış ve bu harçlar %5'lik Na2SO4 çözeltisine 26 hafta süreyle maruz bırakılmışlardır. Yapılan deneysel çalışma sonucunda, S/Ç ve çimento kompozisyonunun harçların sülfatlı sulara karşı performanslarını etkileyen faktörler olduğu tespit edilmiştir. S/Ç oranının sülfata karşı daha az dayanıklı olan ve yüksek $C_3A$ içeren çimentolarda düşük oranda $C_3A$ içeren çimentolara kıyasla daha önemli olduğu tespit edilmiştir.