COMPARISON OF CYCLIC FATIGUE RESISTANCE OF ONE CURVE, HYFLEX EDM, WAVEONE GOLD AND RECIPROC BLUE NICKELTITANIUM ROTARY FILES AT INTRA-CANAL TEMPERATURE

İçi Sıcaklıkta Döngüsel Yorgunluğa Karşı Dirençlerinin Karşılaştırılması

Abstract

Objectives: To compare the cyclic fatigue resistances of One Curve (OC), HyflexEDM (HEDM), WaveOne Gold (WOG), Reciproc Blue (RPC Blue), and nickeltitanium rotary files at intra-canal temperature (35°C).Materials and Methods: Twenty OC (25/.06), 20 HEDM (25/.08), 20 WOG(25/.07) and 20 RPC Blue (25/.08) files were tested for cyclic fatigue at intracanal temperature (35°C). All the instruments were rotated in artificial which weremade of stainless steel with an 60° angle of curvature and a radii of curvatures of5 mm until fracture occurred, and the time to fracture was recorded in secondsusing a digital chronometer and the number of cycles to fracture (NCF) for eachfile was calculated. The Kruskal-Wallis test was performed to statistically analyzethe data by using SPSS 21.0 software. The statistical significance level was set atp

Özet

Amaç: One Curve (OC), Hyflex EDM (HEDM), WaveOne Gold (WOG) ve Reciproc Blue (RPC Blue) NiTi döner kanal aletlerinin kanal içi sıcaklıkta (35°) döngüsel yorgunluğa karşı gösterdikleri dirençlerin karşılaştırılmasıdır. Gereç ve Yöntemler: Yirmi OC (25/,06), 20 HEDM (25/,08), 20 WOG (25/,07) ve 20 RPC Blue (25/,08) kanal aleti kanal içi sıcaklıkta (35°) döngüsel yorgunluk direnci testine dahil edildi. Tüm kanal aletleri, 60° kurvatur açısı ve 5 mm kurvatur yarıçapına sahip paslanmaz çelik yapay kanallarda kırılıncaya kadar döndürüldü. Kırılıncaya kadar geçen süreler djital kronometre ile ölçülüp saniye cinsinden kaydedildi ve kırılıncaya kadarki tur sayıları (KKTS) hesaplandı. SPSS 21.0 yazılımında Kruskal-Wallis testi ile istatistiksel analiz yapıldı. İstatistiksel anlamlılık değeri p