Preparation and dielectric properties of pyroxenic basalt based-glass/mullite composites

Abstract

Pyroxenic basalt-based glass /mullite composites were prepared. The effect of sintering temperatures on crystallized phases were studied by X-ray diffraction patterns; also the details of microstructure and mineralogical constituents were examined by using SEM. The crystallization of augite ss and mullite at low temperature and plagioclase and spinel at higher temperature were observed. Apparent porosity and relative density of the sintered samples were also measured. Measurements of dielectric constants showed preparation of good insulators of samples containing plagioclase and spinel phases.

Özet

Pirosenik basalt esaslı - cam/mullite kompoziteleri hazırlandı. Kristalleşmiş fazlarda sinterlenme sıcaklıklarının etkisi X-ışınları dağılım izlerinde ayrıca mikro yapı ayrıntıları ve mineralojik bileşimi SEM kullanılarak incelenmiştir. Augitess ve mullite'in düşük sıcaklıkta ve "plagioclase" ile "spinel'in yüksek sıcaklıkta kristaleştiği gözlenmiştir. Sinterlenmiş örneklerin bağıl yoğunluğu ve görünür gözenekliliği de ölçülmüştür. Dielektrik sabitleri ölçümlerinden plagioclase ve spinel fazlarını içeren numunelerden iyi yalıtkanlar hazırlandığı görülmüştür.