The Effects of Porogen Agent Size and Interconnection Time on the Mechanical Properties of Gelatin Scaffold

Abstract

In this study, the effects of particle size and interconnection time of porogen agent paraffin spheres on the mechanical properties of macroporous and interconnected scaffolds prepared with combination of molding, phase separation and particle leaching methods were investigated. The mechanical properties of the open-cell foam type scaffolds were measured with a compressive test. It was determined that the increase in the size of paraffin spheres did not significantly change the compressive modulus of the scaffolds. On the other hand, elasticity of the scaffold prepared from 250-425 µm sized paraffin spheres increased significantly (p

Özet

Bu çalışmada, makrogözenekli ve gözenekleri birbirleri ile bağlantılı olarak kalıplama, ısı etkili faz ayrımı ve tanecik uzaklaştırma yöntemleri ile üretilen jelatin bazlı doku iskelelerinde gözenek oluşturucu ajan olan parafin kürelerin boyutu ve bağlantı sürelerinin doku iskelelerinin mekanik özellikleri üzerine olan etkileri incelenmiştir. Sünger formlu ve açık hücreli yapıda olan doku iskelelerinin mekanik özellikleri sıkıştırma testi ile ölçülmüştür. Yapılan ölçümler parafin küre çapındaki artışın doku iskelelerinin sıkıştırma katsayısını istatistiksel olarak anlamlı bir şekilde etkilemediğini göstermiştir. Ancak, parafin kürelerin maruz bırakıldığı ısı etkileşim süresinin 100 dakikadan 400 dakikaya arttırılmasının 250-425 µm çapındaki parafin kürelerle hazırlanan doku iskelesinin elastisite değerini arttırdığı belirlenmiştir (p