Investigation of The Optimum Parameters of Stud Welding on Application to 6060, 6082, 6005 Aluminum Alloys and Investigation of Its Effect on Metallography
- Issue
- 2022 · Sayı: 36
- Pages
- 45–49
- DOI
- —
Abstract
In this study, aluminum studs with a diameter of 5 mm were welded on plates of 5 mm thickness made of 6060, 6082, 6005 aluminum alloys by stud welding method with a capacitor discharge stud welding machine at 70, 80, 90, 100, 110, 120, 130, 140, 150 and 160 volts in an atmosphere unprotected environment. Microstructure pictures of welded samples were taken, their hardness was measured, they were subjected to bending, tensile and torque tests and the results were evaluated.
Özet
Bu çalışmada 6060, 6082, 6005 alaşımlı alüminyum malzemeden 5 mm kalınlıktaki levhaların üzerine 5 mm çapındaki alüminyum saplamalar, saplama kaynak yöntemi ile 70, 80, 90, 100, 110, 120, 130, 140, 150 ve 160 volt değerlerinde kondansatör boşaltmalı saplama kaynak makinesi ile atmosfer korumasız ortamda kaynak edildi. Kaynaklı numunelerin mikro yapı resimleri alınmıştır, sertlikleri ölçülerek, eğme çekme, tork testine tabi tutulmuştur ve sonuçları değerlendirilmiştir.