Investigation of Caking for Boric Acid and Borax Pentahydrate Crystals
- Pages
- 985–996
- DOI
- —
Abstract
In this study, the determination of hygroscopicity and the caking degree, and the tests of mechanical strength, caking, breaking of boric acid (H3BO3) and borax pentahydrate (Na2B4O7.5H2O) crystals produced in pure medium in the CMSMPR (Continuous Mixed-Suspension, Mixed-Product Removal) type crystallizer were performed. Both the H3BO3 and Na2B4O7.5H2O crystals produced in the CMSMPR system were found to have high hygroscopicity, degrees of caking and attrition, and these crystals were highly influenced by moisture and thus deteriorated their habit. Furthermore, when the fluidity conditions determined as a result of caking and breaking tests were evaluated, it was found that H3BO3 crystals were cohesive and Na2B4O7.5H2O crystals were very cohesive. Based on these results, it is seen that H3BO3 and Na2B4O7.5H2O crystals should not be exposed to high humidity in order to avoid caking.
Özet
Bu çalışmada, CMSMPR (sürekli-karıştırmalı, sürekli-ürün çekmeli) tipi kristalizörde, saf ortamda üretilen borikasit (H3BO3) ve boraks pentahidrat (Na2B4O7.5H2O) kristallerinin su alma yeteneği, kekleşme derecesi tayini vemekanik dayanım, kekleşme, kırma testleri yapılmıştır. CMSMPR sisteminde üretilen hem H3BO3 hem deNa2B4O7.5H2O kristallerinin su alma yeteneği, kekleşme, aşınma derecelerinin yüksek olduğu ve bu kristallerinnemden oldukça etkilendiği ve bu nedenle habitinde bozulmalar meydana geldiği görülmüştür. Ayrıca, kekleşmeve kırma testleri sonucunda belirlenen akışkanlık durumları değerlendirildiğinde ise H3BO3 kristallerinin kohezif(yapışan), Na2B4O7.5H2O kristallerinin ise çok kohezif olduğu tespit edilmiştir. Tüm bu sonuçlar esas alındığında,kekleşmeyi önlemek için H3BO3 ve Na2B4O7.5H2O kristallerinin yüksek nem oranlarına maruz kalmamasıgerektiği görülmektedir.