THE PERFORMANCE PROPERTIES OF THE FABRICS PRODUCED FROM CUPRO AND SOME OTHER REGENERATED CELLULOSE FIBERS

CUPRO VE DİĞER BAZI REJENERE SELÜLOZ LİFLERİNDEN ÜRETİLEN KUMAŞLARIN PERFORMANS ÖZELLİKLERİ

Abstract

In this study, performance properties of single jersey knitted fabrics made from viscose, modal, lyocell and cupro yarns are investigated. Performance properties of the fabrics such as fabric weight per unit area, thickness, bursting strength, abrasion resistance, fabric stretch, porosity, air permeability and pilling were evaluated statistically and the importance levels of the relationship between the measured parameters were determined. The highest air permeability value is obtained from cupro fabrics. The highest bursting strength is obtained from lyocell fabrics whereas modal fabrics showed highest abrasion resistance. The results revealed that fiber type is an effective parameter with regard to physical properties of the fabrics.

Özet

Bu çalışmada, viskon, modal, liyosel ve cupro ipliklerden yapılmış süprem örme kumaşların performans özellikleri incelenmiştir. Kumaşların, gramaj, kalınlık, patlama mukavemeti, aşınma direnci, esneme, gözeneklilik, hava geçirgenliği ve boncuklanma özelliği gibi özellikleri istatistiksel olarak değerlendirilmiştir ve ölçülen parametreler arasındaki ilişkinin önem düzeyleri belirlenmiştir. En yüksek hava geçirgenliği cupro kumaşlardan elde edilmiştir. En yüksek patlama mukavemeti lyocel kumaşlardan elde edilirken modal kumaşlar en yüksek aşınma direnci göstermiştir. Sonuçlar, lif tipinin kumaşların fiziksel özellikleri açısından etkin bir parametre olduğunu göstermiştir.

Keywords: Cupro, viskon, modal, lyocel, rejenere selüloz lifi, patlama mukavemeti, hava geçirgenliği, aşınma dayanımı