Influence of Heat Treatment on Microstructure and Mechanical Properties of Plasma Arc Welded AISI 410S Ferritic Stainless Steel

Plazma Ark Kaynağıyla Birleştirilen AISI 410S Ferritik Paslanmaz Çeliğin Mikroyapı ve Mekanik Özelliklerine Isıl İşlemin Etkisi

Abstract

In this study, AISI 410S ferritic stainless steel sheets were joined with plasma arc welding method by using different welding parameters. Heat treatment was applied to plasma welded joints. This study investigated mechanical properties and microstructure of heat treated and non heat treated plasma welded joints. The study revealed that, there have been decreases in tensile strength and hardness of welded joints because of grain coarsening caused by increasing heat input. Hardness and tensile strength of heat treated welded joints were lower and ductility was increasing compared to the ones of non heat treated welded joints.

Özet

Bu çalışmada, AISI 410S ferritik paslanmaz çelik saclar farklı kaynak parametreleri kullanılarak plazma ark kaynak yöntemi ilebirleştirilmiştir. Plazma ark kaynaklı birleştirmelere kaynak sonrası ısıl işlem uygulanmıştır. Isıl işlemli ve ısıl işlemsizbirleştirmelerin mekanik özellikleri ve mikroyapısı incelenmiştir. Çalışma sonucunda, artan ısı girdisine bağlı olarak tane yapısınınirileşmesi nedeniyle kaynaklı birleştirmelerin çekme dayanımı ve sertliğinde azalma meydana gelmiştir. Ayrıca ısıl işlem uygulanankaynaklı birleştirmelerin sertlik ve çekme dayanımı ısıl işlemsiz birleştirmelere göre daha düşük bulunurken, sünekliğin arttığıbelirlenmiştir.