Volume Fraction Effect for the Film Formation of PS/PVAComposites by Monitoring Photon Transmission Technique

PS/PVA Kompozitlerinin Film Oluşumuna Hacim Kesri Etkisinin Işık Geçirgenliği ile İzlenmesi

Abstract

Film forming of the polystrene (PS) doped Poly Vinyl Alcohol (PVA) particles were studied by photon transmission (PT) technique.The films were prepared as a mixture of PS and PVA particles at different compositions ranging from 10 to 100 wt % for the opticalmeasurements at room temperature the film formation process was monitored by measuring the transmitted light intensity (Itr) fromthe samples using PT. The film formation includes two stages: void closure and interdiffusion stages. Percolation model wasemployed to interpret the distribution of PS particles in PVA lattice. Percolation threshold, Rc, was found to be as 0.4 and the volumefraction of PVA as a power law with exponent 1.01 which is very close to the predicted value, 1.00, by the percolation theory.

Özet

Polistren (PS) katkılı Poli Vinil Alkol (PVA) dağılımının film oluşum süreci foton geçirgenliği (PT) teknikle incelenmiştir. Filmler,oda sıcaklığında optik ölçümler için ağırlıkça %10 ile %100 arasında değişen farklı bileşimlerde PS ve PVA dağılımının bir karışımıolarak hazırlandı. Film oluşum süreci, PT kullanılarak numunelerden geçen ışık şiddeti (Itr) ölçülerek izlendi. Film oluşumunun ikiaşamada gerçekleştiği gözlemlendi: boşluk kapanması ve difüzyon aşamaları. PVA kafesinde PS parçacıklarının dağılımınıyorumlamak için süzme modeli kullanıldı. Süzme teorisine göre, perkolasyon eşiği Rc 0,4 ve PVA'nın hacim kesri için 1.01 tahminedilen değer olan 1,00'e çok yakın bulunmuştur.