The investigation of the strength of acrylic resins repaired with fiber-reinforced composite and traditional, repair materials

Fiber ile güçlendirilmiş kompozit rezin ve geleneksel tamir materyalleriyle tamir edilen akrilik rezinlerin dirençlerinin incelenmesi

Abstract

In this study, it was investigated that the transverse strength of acrylic resin test specimens repaired with Splint-It, heat-cured and autopolimerising acrylic resin. Intact heat-cured specimens were used as control group. Intact and repaired acrylic resin specimens were tested after storage in distilled water at room temperature for 17 days. In testing procedure, a load was applied centrally to the specimens at the cross-head speed of 5mm/min using Hounsfield Tensometer. The values obtained were compared statistically. Statistically, significant differences (p0,05) were found between the control group and Splint-It group. However; when these two groups were compared to the other groups, it was found that they exhibited a significant difference (p

Özet

Bu çalışmada; ısı ile polimerize olan akrilik rezin, otopolimerizan akrilik rezin ve Splint-It ile tamir edilmiş olan akrilik rezin örneklerin dirençleri incelenmiştir. Hiçbir tamir işlemi uygulanmaksızın sağlam olarak ayrılan örnekler kontrol grubunu oluşturmuştur. Sağlam ve tamir edilmiş akrilik rezin örnekler 17 gün süreyle oda sıcaklığındaki saf suda bekletildikten sonra test edilmişlerdir. Test işleminde, örneklere Hounsfield tensometresi kullanılarak 5mm/dakika başlık hızı ile kuvvet uygulanmıştır. Elde edilen değerler istatistiksel olarak karşılaştırılmıştır. Yapılan istatistiksel değerlendirme sonucunda; gruplar arasında önemli bir farklılık olduğu (p0,05), bu iki grup ile diğer tamir materyalleri arasında önemli bir farklılık olduğu (p