A comparison of tensile strengths and elongation at break of some elastomeric impression materials

Bazı elastomerik ölçü maddelerinin uzama değeri ve çekme dayanıklılığının karşılaştırılması

Abstract

The tensile strengths and ultimate elongation at break of five elastomeric impression materials were evaluated. Each impression material was mixed according to the manufacturers instructions, and formed by placing on aluminum die of 50 mm. long, 10 mm. wide, and 3 mm. thick on a glass slab. A second glass slab was placed on top of the die. The specimens, were placed in 32 $circ$C+ 0.1$circ$C water bath for 2 minutes longer than time recommended by the manufacturer for the material to remain in the mouth (American dental association specification No. 19). Test were performed immediately after the specimens were removed from the die. Tensile strengths were determined on a Hounsfield pull and press machine at a crosshead speed of 10 inchs/minute. The results of ANOVA demostrated a statistically significant difference among the elastomeric impression materials (p

Özet

Beş elastomerik ölçü maddesinin uzama değeri ve çekme dayanıklılığı değerlendirildi. Her ölçü maddesi üreticinin önerdiği şekilde karıştırıldı. 50 mm. uzunluğunda, 10 mm. genişliğinde ve 3 mm. kalınlığında hazırlanmış aliminyum kalıp içinde 2 cam arasında sıkıştırıldı. 32$circ$C+0.1$circ$C su banyosunda sertleşmeye bırakıldı. Sertleşme için imalatçının ağız ortamında önerdiği süreden 2 dakika daha fazla tutuldu. Sertleşme sonunda örnekler derhal kalıptan çıkarılarak başlık hızı 10 inch/dak. olan Hounsfield çekme sıkıştırma makinasına bağlandı (American Dental Association Spesification No: 19) Çekme dayanıklılığı ve uzama değerleri için yapılan varyans analizinde materyaller arasında farklılık olduğu bulunmuştur (p