Effect of different application methods of composite resings on microhardness

Farklı uygulama yöntemlerinin kompozit rezinlerin mikrosertlikleri üzerine etkisi

Abstract

Purpose: The purpose of this study was to investigate the effect of different application methods of composite resins on microhardness. Materials and Methods: Test samples (2mm thick, 6mm in diameter, n=12) were prepared by using a hybrid composite (Filtek Z250, 3MESPE, St. Paul MN, USA). Following applications were performed on the surface of the specimens. Groupl: Direct application (only composite application). Group2: Composite application under mylar strip. Group3: Composite application with Panavia F Oxyguard II (Kuraray Medical Inc, Japan). Group4: Composite application with Biscover (Bisco, Inc. Schaumburg, IL, USA). The hardness test was performed using a digital microhardness tester (Buehler, Lake Bluff, Illinois, USA)(load: 500 g; dwell time: 15 seconds). All samples were measured from the top and the bottom of the composite discs. Data were analyzed by using Studentt-test, One-Way ANOVA and Tukey's tests (p

Özet

Amaç: Bu çalışmanın amacı, farklı uygulama yöntemlerinin kompozit rezinlerin mikrosertliğine olan etkisinin incelenmesidir. Gereç ve Yöntem: 2mm kalınlığında, 6mm çapında (n=12) test örnekleri, hibrid bir kompozit (Filtek Z250, 3MESPE, St. Paul MN, USA) kullanılarak hazırlandı. Örneklerin yüzeyine şu uygulamalar yapıldı: Grupl: Sadece direkt kompozit uygulaması yapıldı. Grup2: Mylar strip altında kompozit uygulandı. Grup3: Panavia F Oxyguard II (Kuraray Medical Inc, Japan) ile kompozit uygulaması yapıldı. Grup4: Biscover (Bisco, Inc. Schaumburg, İL, USA) ile kompozit uygulaması yapıldı. Sertlik testi, dijital mikrosertlik test cihazı(Buehler, Lake Bluff, Illinois, USA) (kuvvet: 500 g; dwell time: 15 saniye) kullanılarak gerçekleştirildi. Tüm örnekler üst ve alt yüzeylerinden ölçüldü. Veriler Student t-test, One-Way ANOVA ve Tu keys test ile analiz edildi (p