Tear strength of silicone-based elastomeric impression materials

Silikon esaslı elastometrik ölçü materyallerinin yırtılma dayanıklılığı

Abstract

The tear resistances of one addition (Provil L) and two condensation (Deguflex CS light and Coltex extrafine) type of silicone impression materials were tested. The effects of the paste proportioning and the crosshead speed on the tear strength were also investigated. Trouser-legged specimens were prepared using three different paste proportions (recomended length by manufacturers and within ±20 % of the recom¬mended length ) and were subjected to two different crosshead speeds (500 mm/min and 100 mm/min). The results were evaluated by using two way ANOVA and the differences among the groups were statistically significant (p

Özet

Çalışmada, iki adet kondansasyon (Deguf-lex CS light ve Coltex extrafine) ve bir adet katılma silikonu (Provil L) kullanılarak, silikon esaslı elastomerik ölçü materyallerinin yırtılma dayanıklılığı test edilmiş; ana madde-katalizör oranı ve yırtılma testinde kullanılan çekme hızının etkisi de değerlendirilmiştir. Üreticinin önerdiği ana madde-katalizör oranı ile %20 oranında değiştirilen katalizör miktarları ile hazırlanan pantolon bacağı şeklindeki örneklere, iki farklı çekme hızı (500 mm/ dak ve 100 mm/dak) kullanılarak yırtılma testi uygulanmıştır. Her örnek için hesaplanan yırtılma daya¬nıklılığı değerleri iki yönlü varyans analizi kullanılarak değerlendirilmiş; gruplar arasındaki farklılığın istatistiksel olarak anlamlı olduğu sonucuna varılmıştır (p