Evaluation of antibacterial effects of glass-ionomer based restorative materials

Cam-ionomer esaslı restoratif materyallerin antibakteriyel etkilerinin değerlendirilmesi

Abstract

The aim of this in vitro study was to evaluate the antibacterial activity of 4 different glass ionomer based restorative materials and one com-posite resin on Streptococcus mutans, Staphylococcus aureus, Lactobacillus casei and Bacillus subtilis by using the agar plate diffusion method. 10 plates were used for each bacterium that each one included 6 standard holes 4,5 mm diameter and 2 mm thickness. Disk shape specimens were prepared on Teflon plates and were placed into the holes. One hole was left empty for control. Plates were incubated at 37$circ$C and observed for 24 hours, 48 hours and 7 days and inhibition zones were measured. The data was evaluated by Variance Analysis and Duncan Test. Statistically analysis showed sig-nificant differences between Ketac Fill Aplicap and Vitremer groups (P

Özet

Bu in vitro çalışmanın amacı; 4 farklı cam ionomer esaslı restotatif materyalin ve bir kompozit rezinin Streptococcus mutans, Staphylococcus aureus, Lactobacillus casei ve Bacillus subtilis üzerine antibakteriyel etkilerinin agar diffizyon yöntemi kullanılarak incelenmesidir. Çalışmada, her bir bakteri için üzerinde 4,5 mm genişliğinde ve 2 mm kalınlığında 6 yuvanın bulunduğu 10 plaka kullanıldı. Disk şeklindeki örnekler teflon kalıplar üzerinde hazırlandıktan sonra bu yuvalara yerleştirildi. Bir yuva boş bırakılarak kontrol grubu olarak incelendi. Plakalar 37$circ$C de inkübe edilerek oluşturdukları inhibisyon bölgeleri 24 saat, 48 saat ve 7 gün boyunca izlendi. Elde edilen veriler Varyans anallizi ve Duncan testi kullanılarak değerlendirildi. İstatistiksel incelemeler Ketac Fiil Aplicap ve Vitremer grupları arasında önemli farklar olduğunu gösterdi (P