EVOLUTION OF BARITE ORE MINED IN TURKEY IN THE PRODUCTION OF BARIUM CONTAINING PIGMENTS

TÜRKİYE'DE ÜRETİLEN BARİT CEVHERİNİN BARYUM İÇEREN PİGMENTLERİN ÜRETİMİNDE DEĞERLENDİRİLMESİ

Abstract

Barite and barium containing chemicals are important materials which are used in wide rangingapplications in chemical and manufacturing industries such as pigment, paper brightener, glass additive,plastics filler and drilling fluids. The aim of the study was to evolution of using barite mineral mined inTurkey as a raw material in the production of barium containing pigments. BaSO4 which is used in thepigment production was obtained from barite mineral by black-ash and leaching methods. In the black- ash process, to produce barium sulfide which is soluble in water barite was reduced with coal or cokeor graphite between 1000 C and 1300 C in a kiln and black color ash was obtained. After bariumsulphide solution was leached from black ash with hot water at 90 C for 30 minutes, BaSO4 powder wasprecipitated by addition of Na2 SO4 in this solution. The white and green colour pigments were producedby adding ZnSO4 and Cr2 O 3 into synthesized BaSO4 powder. The colour performances of resultingpigments were evaluated by using in the single firing transparent glazes and were investigated the usingpotential as ceramics colorants. In transparent glaze, white and green colours which are intense,thermally and chemically stable were obtained. Results demonstrated that barite mined in Turkey canbe used in pigment production which has high value added.

Özet

Barit ve baryum içeren kimyasallar, sondaj çamuru, dolgu malzemesi, pigment, kağıt beyazlatmave cam ilavesi olarak kimyasal ve üretim endüstrilerinde geniş uygulama alanlarında kullanılan önemlimalzemelerdir. Bu çalışma, Türkiyede çıkartılan barit cevherinin seramik pigment üretimindehammadde olarak değerlendirilmesini amaçlamaktadır. Pigment üretimi için gerekli olan BaSO4 , black- ash ve liç metoduyla barit cevherinden elde edilmiştir. Black-ash prosesinde, suda çözünebilen baryumsülfit üretebilmek için barit hammaddesi kok, kömür veya grafit ile 1000o C-1300o C sıcaklıkları arasındaindirgenmiş ve siyah renkli kül elde edilmiştir. Siyah renkli külün 90o C de 30 dak sıcak suda liç edilerekbaryum sülfit (BaS) çözeltisi elde edildikten sonra, NaSO4 ilave edilerek BaSO4 tozu çöktürülmüştür.Sentezlenen BaSO4 tozuna ZnSO4 ve Cr2 O 3 ilavesi yapılarak beyaz ve yeşil renkli pigmentlerüretilmiştir. Pigmentlerin tek pişirim şeffaf sırda renk performansları incelenmiş ve seramikrenklendiricisi olarak kullanım potansiyeli araştırılmıştır. Şeffaf tek pişirim sırlarında yoğun, termal vekimyasal kararlılığı yüksek olan beyaz ve yeşil renkler elde edilmiştir. Sonuçlar, ülkemizde çıkartılanbaritin katma değeri yüksek olan pigment üretiminde kullanılabileceğini göstermiştir.