XRD RAMAN AND Uv-vis SPECTROSCOPICAL ANALYSIS OF NANOSTRUCTURED CdS:Li FILMS

Abstract

CdS and CdS:Li films were produced by means of ultrasonic spray pyrolysis (USP) method by spraying on glass substratesheated up to 340±5 ◦C. LiCl in three different rates was added into the preliminary solution while producing the CdS:Lifilms. The effect of Li on the structural and optical characteristics of the CdS film was analyzed. XDR spectra showed thatthe crystallization degree decreases while lithium is 15% and increases when lithium rate increases. The crystallite sizeswere calculated to be in the range of 60-85 nm. SEM photographs showed that the contribution of Li changed surfaceappearances of films and their particle size. All films exhibited the Raman peaks centered 298 and 590 cm-1and the peakprofiles were almost symmetric. The optical band gap and Urbach energy values of these films were determined. Themaximum transmittance was found to be almost 80% for the visible region. LiCl which was added to the preliminarysolution changed the optical characteristics of CdS film.