Klorür içeren çözeltilerde aluminyum için korozyon inhibitörlerinin değerlendirilmesi

Evaluation of corrosion inhibitors for aluminum in chloride containing solutions

Abstract

Research has been conducted on the corrosion inhibition of commercial aluminum in aqueous solutions containing 100 ppm $Cl^-$ ion alone or mixed with one of the following five inhibitors covering the concentration range of 1000-5000 ppm between pH 5 and 9: sodium chromate, sodium nitrite, sodium molybdate, sodium orthophosphate and sodium tetraborate. Compared with other inorganic inhibitors tested, chromate was found to be the most effective. The chromate was taken as a reference inhibitor against which the effectiveness of the binary and ternary inhibitor systems was compared. Comparison was made on the basis of inhibiton efficiency determined from the cathodic polarization data. Of all the inhibitor systems tried, sodium tetra borate-sodium chromate was found to be the most effective binary inhibitor blend, the effectivenes of which is equal that of sodium chromate alone in all ratios experienced.

Özet

Ticari alüminyumun 1000 ppm $Cl^-$ iyonu içeren sulu çözeltilerdeki korozyonunun inhibisyonu pH: 5-9 arasında, aşağıda verilen maddeler için 1000-5000 ppm konsantrasyon aralığında incelendi. Sodyum kromat, sodyum nitrit, sodyum molibdat, sodyum orto-fosfat ve sodyum tetraborat. Bu inorganik inhibitörler arasında en etkin olanın kromat olduğu belirlendi ve bu ikili ve üçlü inhibitor sistemlerinin etkinliklerini karşılaştırmada referans olarak kullanıldı. Inhibisyon etkinliği katodik polarizasyon verilerinden yararlanılarak belirlendi. Çalışılan bu inhibitor sistemlerinden en etkili olanın sodyum tetraborat-sodyum kromat karışımı olduğu ve inhibisyon etkinliği açısından bu karışımın denenen tüm oranlarda kromat'a eşdeğer sayılabileceği saptandı.