The effect of shielding gas mixture on tensile strength of MIG/MAG welded construction steel (St52-3)
- Pages
- 9–15
- DOI
- —
Abstract
In this study, St52-3 construction steel has been welded with MIG/MAG welding method that has a wide range of application in industry. The mixture of the shielded gasses in MIG/MAG welding process is very important for the quality of the weld. In the study, three different mixture of gases were used. These mixture of these gas were $80Ar+18CO_2+2O_2$, $88Ar+10CO_2+2O_2$ and $93Ar+5CO_2+2O_2$. After welding procedure the effect of the mixture on the tensile strength was investigated. The results of the tests showed that the mixture of $88Ar+10CO_2+2O_2$ shielding gas gives highest tensile strength while $93Ar+5CO_2+2O_2$ shielding gas mixture results in lowest tensile strength.
Özet
Bu çalışmada 4 mm kalınlığındaki St52-3 yapı çeliği endüstride yaygın olarak kullanılan MIG/MAG kaynak yöntemi ile birleştirilmiştir. MIG/MAG kaynak yönteminde koruyucu gazlar büyük bir öneme sahiptir. $80Ar+18CO_2+2O_2$, $88Ar+10CO_2+2O_2$ ve $93Ar+5CO_2+2O_2$ olmak üzere üç farklı gaz karışımları kullanılmıştır. Seçilen bu gazlarla MIG/MAG kaynağı yapıldıktan sonra çekme deney numuneleri hazırlanmış ve bunların çekme dayanımı özellikleri incelenmiştir. Çekme deney sonuçlarına göre, $88Ar+10CO_2+2O_2$ karışım gazı ile en yüksek $93Ar+5CO_2+2O_2$ karışım gazı ile de en düşük çekme dayanımı değerleri elde edilmiştir.