Influence of sample length change on the compressive strength and strain at compressive strength of mortars made with various water-binder ratio

Farklı su bağlayıcı oranında hazırlanan harçlarda numune boy değişiminin basınç dayanımı ve birim kısalma üzerindeki etkisi

Abstract

In this work, influence of sample length change on the compressive strength and strain at compressive strength was investigated using portland cement mortar made with various water-binder ratio. Cylindirical mortar specimens made with water-binder ratio of 0.25, 0.30, 0.40, 0.50 and 0.60 were prepared with a constant diameter of 5 cm and various length of 2.5, 5, 7.5, 10, 12.5and 15 cm. As a result of testing measurement using these specimens, it was obseved that strength reduced as water-binder ratio increased. In addition, it was observed that as the length-diameter ratio of sample reduced the compressive strength and strain at compressive strength increased. It should be noted that increase in the strain at compressive strength was much more than the increase in compressive strength.

Özet

Bu çalışmada, farklı su-bağlayıcı oranlarında hazırlanan harç karışımlarda, numune boy değişiminin, basınç dayanımı ve basınç dayanımındaki birim deformasyon üzerindeki etkisi incelenmiştir. S/B oranları 0.25, 0.30, 0.40, 0.50 ve 0.60 olan karışımlar çapları sabit (5 cm) olan, boyları 2.5, 5, 7.5, 10, 12.5 ve 15 cm şeklinde değişen silindir şeklindeki kalıplara dökülerek, farklı boylarda harç numuneler elde edilmiştir. Bu numuneler üzerinde gerçekleştirilen deneyler sonucunda, su-bağlayıcı oranının artmasıyla basınç dayanımının düştüğü görülmüştür. Ayrıca numune boyu-çap (l/d) oranı azaldıkça basınç dayanımı ve basınç dayanımındaki birim kısalmanın arttığı gözlenmiştir. Boy-çap oranı azaldıkça, basınç dayanımına karşılık gelen basınç dayanımındaki birim kısalma artmıştır, ancak basınç dayanımındaki birim kısalma basınç dayanımına göre çok daha fazla etkilenmiştir.