Influence of resin cement applicated on fiber reinforced composite (FRC) post surface on the retantion of post-core restoration

Betül ÖZÇOPUR,Andaç Barkın BAVBEK,KEZBAN ÇELİK,Meltem ÖZER,Gürcan ESKİTAŞCIOĞLU

Abstract

Background: The aim of this in vitro study was to evaluate the push-out bond strength of resin cement applicated FRC post to core material. Methods: 80 FRC post (Snowpost, USA) were divided into four groups. First three groups (n=20), specimen surfaces were applicated with different resin cements (Panavia F-Kuraray, Super Bond C&B- Kuraray, Clearfil SA- Kuraray), whereas the last group used as a control group. After apply a dual cure adhesive (Clearfil SE-Kuraray) onto coronal post surfaces, the specimens were restored with core material in 6 mm diameter (Clearfil Core Build Up, Kuraray). The specimens were cut into 1 mm-thick slabs and retantive ability of post-cores were tested with push-out test by universal testing machine at a crosshead speed of 1mm/min. The forces required for dislodgement of the post were recorded. Data were analyzed using ANOVA and the Duncan multiple comparison tests (=0.05). Results: Resin cement application had a significant influence on push-out bond strength of post-core restoration (p<0.05). Panavia F (4,77±1,58 MPa) and Clearfil SA (7,18±3,14 MPa) were found significantly different from eachother (P<0.05), whereas SuperBond C&B (5,72±2,98 MPa) demonstrated similar results with Panavia F (4,77±1,58 MPa) and Clearfil SA (7,18±3,14 MPa) (P>0.05). All the groups showed higher results than the control group (3,57±1,88) (p<0.05). Conclusions: In this study, it was observed that resin cement application can increase the push-out strengths of FRC posts tested. The higher bond strengths in cement applicated groups showed that cement application on post surface may positively influence the post-to-core strengths.

Özet

Amaç: Bu in vitro çalışmanın amacı rezin siman uygulanmış FRC post ile kor materyali arasındaki push out bağlanma dayanımını incelemektir. Gereç ve Yöntemler: 80 FRC post (Snowpost, USA) dört gruba ayrıldı. İlk üç grupta (n= 20) örneklerin yüzeyine farklı simanlar uygulandı ( Panavia F- Kuraray, Super Bond C&B- Kuraray, Clearfil SAKuraray), son grup kontrol grubu olarak kullanıldı. Post yüzeylerine dual-cure adheziv uyguladıktan sonra (Clearfil SE- Kuraray) örnekler 6 mm çapında kor materyali ile restore edildi (Clearfil Core Build Up, Kuraray). Örnekler 1 mm kalınlığında kesildi ve post-kor bağlantısı universal test makinası ile 1 mm/dak hızda test edildi. Postların yer değiştirmesi için gerekli kuvvetler kayıt edildi. Veriler ANOVA ve Duncan çoklu karşılaştırma testleri ile analiz edildi (=0.05). Bulgular: Rezin siman uygulamasının post-kor restorasyonun push out bağlanma dayanımında etkisi önemlidir (p 0.05). Bütün gruplar kontrol grubundan (3,57±1,88) daha yüksek bağlanma dayanımı göstermiştir (p<0.05). Sonuç: Bu çalışmada rezin siman uygulamasının FRC postun kor materyaline push-out bağlanma dayanımını artırdığı gözlenmiştir. Post yüzeyine siman uygulanan gruplarda yüksek bağlanma dayanımı gözlenmesi siman uygulamasının post-kor bağlantısını pozitif yönde etkileyebileceğini göstermektedir