The Effect of Synthesis Conditions on Calcium Silicate Bioceramic Materials
- Pages
- 727–737
- DOI
- —
Abstract
In this study, calcium silicate bioceramic materials of various Ca/Si ratios were prepared using tetraethyl orthosilicate and calcium nitrate by a hydrothermal synthesis method, taking into consideration cost-effective and environmentally friendly, ‘green’, synthesis rules. For comparison purposes, sol-gel synthesis method was also used. Calcium silicate bioceramic materials produced by both methods were calcined at 600°C and 950°C. Fourier Transform Infrared Spectroscopy, Thermogravimetric Thermal Analysis, Field Emission Scanning Electron Microscopy and X-ray Diffraction methods were used to characterize calcium silicate bioceramic materials. The characterization results validated the formation of calcium silicate materials.
Özet
Bu çalışmada, çeşitli Ca/Si oranlarındaki kalsiyum silikat biyoseramik malzemeleri, düşük maliyetli ve çevre dostu "yeşil" sentez kuralları göz önünde bulundurularak, bir hidrotermal sentez yöntemi ile hazırlanmıştır. Karşılaştırma amacıyla sol-gel sentez metodu da kullanılmıştır. Başlangıç materyali olarak tetraetil ortosilikat ve kalsiyum nitrat kullanılmıştır. Her iki yöntemle üretilen kalsiyum silikat biyoseramik malzemeleri 600 °C ve 950 °C'de kalsine edilmiştir. Fourier Dönüşümü Kızılötesi Spektroskopisi, Termogravimetrik Termal Analiz, Alan Emisyon Taramalı Elektron Mikroskobu ve X-Işını Kırınımı metodları kalsiyum silikat biyoseramik malzemeleri karakterize etmek için kullanılmıştır. Karakterizasyon sonuçları kalsiyum silikat malzemelerinin oluşumunu doğrulamıştır.