The effect of induction hardening and austempering of spheroidal cast iron on wear resistance
- Pages
- 179–187
- DOI
- —
Abstract
In this study, pearlitic cast iron with spheroidal graphite specimens were heated to 900 °C for 10 seconds by a pancake inductor and then some of the specimens were water quenched and the others were austempered at 225 ° C and 375 °C in the salt bath. After heat treatment, investigation of microstructure and measurement of specimens hardness were done. it was seen that an important increase in the values of specimens hardness were observed. By doing wear experiments on the ali specimens, vveight losses were determined. The least weight loss was noticed in specimens water quenched.
Özet
Bu çalışmada, perlitik küresel grafitli dökme demir numunelerin yüzeyleri yassı tabanlı indüktörle 900 °C' ye 10 saniye süreyle ısıtıldıktan sonra bir kısmı suda sertleştirilmiş, bir kısmı da 225 ° C ve 375 °C sıcaklıklardaki tuz banyolarında ostemperlenmiştir. Isıl işlemden sonra numunelerin mikroyapıları incelenmiş ve sertlikleri ölçülmüştür. Isıl işlem sonrasında numunelerin sertlik değerlerinde önemli artışlar olmuştur. Tüm numunelerde aşınma testleri yapılarak ağırlık kayıpları belirlenmiştir. Aşınma sonrası en az ağırlık kaybı sertleştirilen numunelerde gözlenmiştir.