Investigation of Wear Behaviors of SiO2 Reinforced Aluminium Composites Produced by Pressureless Infiltration Method

Basınçsız İnfiltrasyon Yöntemiyle Üretilen SiO2 Takviyeli Alüminyum Kompozitlerin Aşınma Davranışlarının İncelenmesi

Abstract

In this study, the wear behaviors of SiO2 reinforced AA7075 matrix composites produced by pressureless infiltration method were investigated in the scope of the work, 10%, 20%, 30%, and 40% SiO2 were added into AA7075 Al alloy and produced by infiltration method. Produced samples’ density values were measured by Archiment method, hardness values were measured in micro hardness device under 2 N load. Wear tests were performed using 1 ms-1 sliding speed at five difference sliding distance under 15 N load by pin-on-disc type apparatus. As a result of the study, the density values were decreased by increasing SiO2 amount and hardness values were increased by increasing SiO2 amount. In addition the weight loss and friction coefficient were decreased depending on increasing of SiO2 amount.

Özet

Bu çalışmada, basınçsız infiltrasyon yöntemiyle üretilmiş olan SiO2 takviyeli AA7075 matrisli kompozitlerin aşınma davranışları incelenmiştir. Çalışma kapsamında 7075 Al alaşımı içerisine %10, 20, 30 ve 40 takviye-hacim oranı oluşturacak şekilde farklı oranlarda SiO2 ilave edilerek infiltrasyon yöntemiyle üretilmiştir. Üretilen numunelerin yoğunluk ölçümleri Arşimet prensibine göre, sertlik ölçümleri ise mikro sertlik cihazında 2 N yük uygulanarak Vickers olarak ölçülmüştür. Aşınma testleri pin-on-disk tipi aşınma cihazında 1 ms-1 kayma hızında 15 N yük altında beş farklı kayma mesafesinde test edilmiştir. Yapılan çalışmalar sonucunda, takviye elemanı olarak AA7075 alaşımına ilave edilen SiO2 miktarı arttıkça, kompozitlerin yoğunlukları azalırken sertlikleri artmaktadır. Bununla birlikte, ilave edilen SiO2 miktarındaki artışa bağlı olarak alüminyum kompozitlerin ağırlık kaybının ve sürtünme katsayılarının da azaldığı belirlenmiştir.