Investigation of the Effect of Hydrogen Addition to Argon Shielding Gas on Weld Zone Morphology of TIG Welded 316L Stainless Steel

316L Paslanmaz Çeliğin TİG Kaynağında Koruyucu Argon Gazına Hidrojen İlavesinin Kaynak Bölgesi Tane Morfolojisine Etkilerinin Araştırılması

Abstract

In this study, hardness, depth of penetration and microstructure of TIG welded 316L austenitic stainless steel plate were investigated. Welding was carried out by using pure Ar, Ar+1,5%H2 and Ar+5%H2 gases. It was seen that weld penetration increased with increasing H2 content and grains were directed towards welding center from melting boundary. Increase in grain growth and HAZ width were observed with increasing H2 content. Hardness in weld deposit surface and deposit inner sections were different due to the difference in grain orientation

Özet

Bu çalışmada 316L Östenitik paslanmaz çelik levhaların yüzeyine TIG kaynak yöntemi ile dikişler çekilerek sertlik, nüfuziyet ve mikroyapıları incelenmiştir. Kaynak işlemi, saf argon, argon içerisine % 1,5 ve 5 hidrojen ilave edilerek gerçekleştirilmiştir. İncelemeler sonucunda argon koruyucu gazına ilave edilen hidrojen miktarının artmasıyla nüfuziyetin arttığı tespit edilmiştir. Mikroyapı görüntüleri değerlendirildiğinde, ergime sınırından itibaren kaynak merkezine doğru belirgin yönlenmelerin olduğu görülmüştür. ITAB’a bakıldığında hidrojen miktarının artışına paralel olarak tane irileşmesinde artış ve ITAB’de genişleme olduğu görülmüştür. Kaynak yüzeyinden ve kesitinden yapılan sertlik ölçümleri yönlenme farkından dolayı farklı değerlerde bulunmuşlardır.