Investigation of the İmpact Amount of an Aluminum Sheet With TIG Welding

TIG Kaynağı Yapılan Alüminyum Bir Sac Parçanın Çarpılma Miktarının İncelenmesi

Abstract

Welded joints have a wide range of applications in industrial applications. Many different welding methods are used in parts manufactured using welding and all of these methods have a sudden heat input in common. With the sudden heat input, the material is subjected to different stresses and a distortion is seen in the material as these stresses cannot be removed. In this study, the relationship between distorted current input and distortion is investigated in an aluminum sheet part welded by TIG-Argon welding method. As a result of the applications, the amount of distortion on the parts was determined and the variation of the distortion amount was examined for the parts with the same dimensions depending on the current amount.

Özet

Kaynaklı birleştirmeler sanayi uygulamalarında oldukça fazla uygulama alanlarına sahiptir. Kaynak kullanılarak imal edilen parçalarda birçok farklı kaynak yöntemi kullanılmaktadır ve bu yöntemlerin hepsinde ortak olarak ani bir ısı girdisi olmaktadır. Ani ısı girdisiyle beraber malzeme farklı gerilmelere maruz kalır ve bu gerilmelerin giderilememesi sebebiyle malzemede bir çarpılma(distorsiyon) görülür. Bu çalışmada TIG-Argon kaynak yöntemiyle alın kaynağı yapılan bir alüminyum sac parçada değişen akım girdisi ile çarpılma arasındaki ilişki incelenmiştir. Yapılan uygulamalar sonucunda parçalar üzerindeki çarpılma miktarları tespit edilerek aynı boyutlardaki parçalar için akım miktarına bağlı olarak çarpılma miktarının değişimi incelenmiştir.