Influences of use of fly ash in concrete

Abstract

Usability of fly ash, which is an industrial by-product, in concrete as an additive was investigated. The concrete specimens were produced with fly ash of Çayırhan Power Plant, aggregates of Eskişehir region, and PKÇ/B 32.5R cement. The cement dosages were 300, 350 and 400 kg/$m^3$, the cement replacement of fly ash are 20 and 40 %. Slump, VeBe, Flow-test and fresh unit weight tests were carried out during specimen production when it is fresh. The mechanical and physical influences of fly ash on the concrete properties were determined after production of 7, 28 and 60 days.

Özet

Endüstriyel bir atık olan uçucu külün betonda bağlayıcı malzeme olarak kullanımının özeliklere etkisi araştırılmıştır. Bu amaçla Çayırhan Termik Santrali 'nden elde edilen uçucu kül, Eskişehir bölgesi agregaları ve PKÇ/B 32.5R çimentosu kullanılarak beton numuneleri üretilmiştir. Numuneler 300, 350, 400 kg/$m^3$ dozaj ve bu dozajların her biri için çimento yerine % 20 ve % 40 oranında uçucu kül katılarak elde edilmiştir. Üretim sırasında taze betonlarda çökme, VeBe, yayılma ve birim ağırlık deneyleri yapılmış ve sonuçları değerlendirilmiştir. Laboratuvar ortamında bekletilen numuneler 7, 28 ve 60 günün sonunda yapılan deneylerle uçucu külün beton üzerindeki fiziksel ve mekanik etkileri belirlenmiştir.