Effect on fatigue behaviour of boronising and shot peening in ferrous based P/M materials

Borlama ve bilyalı dövmenin demir esaslı T/M malzemelerde yorulma davranışına etkisi

Abstract

Ferrous based materials manufactured by P/M method are widely used in industry. These materials are very important no machining, can be use for self-lubricated property as journal bearing material, in addition medical etc. applies. In this study, powder metal parts were manufactured from composites ferrous based FeCu-Graphite by P/M method particulate reinforced. Fatigue test samples were manufactured and boronising and boronising+shot peening was applied to some samples. Fatigue properties of these parts were investigated and compared on bending fatigue test rig.

Özet

T/M yöntemiyle üretilmis toz metal parçalardan, demir esaslı malzemeler endüstride yaygın bir sekilde kullanılmaktadır. Bu malzemeler üretim sonunda hiçbir talaslı islem gerektirmeden son ürünün seklini alması, kendinden yağlama özelliği olması nedeniyle yatak malzemesi olarak ve ayrıca tıp vb. endüstri uygulamalarında kullanılabilmesi açısından önem teskil etmektedir. Bu çalısmada, demir esaslı FeCu-Grafit kompozitinden toz metal parçalar üretilmistir. Bu parçalardan yorulma deney numuneleri üretilip, bazılarına borlama ve borlama+bilyalı dövme islemi uygulanmıstır. Bu parçaların eğmeli yorulma deney cihazında yorulma özellikleri incelenip birbiriyle karsılastırılmıstır.