Fe-Al-Ti-Composites Produced By powder Metallurgy methods with the Microwave Sintered The Joining By Diffusion Bonding Methhod
- Pages
- 21–29
- DOI
- —
Abstract
In this study, the joining by diffusion bonding method mixtures of iron aluminium and iron aluminium titanium microwave sintered by using electrolytic Cu interlayer. Temperature, pressure and time factor by cahanging the sutable welding paremeters bonding. The joined pairs of 40-60 N/mm2 shear strength and hardness was found to be an avarage 67 HV. Leo microstructures of the samples made with scanning electron microscopy and EDX analysis of the identifiend compound. Produced by the methot of powder metallurgy iron aluminates, using a diffısion welding without intermediate layer not bonding, however, the intermediate layer of Cu diffusion welding applications have been sucsessfully used
Özet
Bu çalışmada, mikrodalga sinterleme kullanılarak üretilen Fe-Al-Ti metalik toz karışımları, aratabakasız ve elektrolitik Cu kullanılarak yapılan difüzyon kaynağında sinterleme sıcaklığının, kaynağın dayanımına ve sertliğine etkisi araştırılmıştır. Cu aratabaka kullanılarak yapılan difüzyon kaynağında birleştirme bölgesinin kesme mukavemeti ortalaması 46 MPa ve bu bölgelerden alınan mikrosertlik ortalama değeri ise 67 HV olarak ölçülmüştür. Numunelerin içyapı analizi sonucu, matris yapıda bulunan Fe, Al ve Ti ile Cu aratabakanın yayınım reaksiyonuna girdiği görülmüştür. Toz metalurjisi metodu ile üretilmiş olan Fe-Al-Ti karışımları, ara tabaka kullanmadan difüzyon kaynağı ile birleştirilememiştir. Ancak, Cu ara tabakalı difüzyon kaynağı uygulamalarında başarılı sonuçlar alınmıştır.