Metal powder production and investigation of parameters of production variables by laval type a new nozzle design
- Pages
- 69–76
- DOI
- —
Abstract
In this study, annular slotted type of supersonic nozzle has been developed and tested for powder production by gas atomization. Atomization experiments have been carried out in the Gas Atomization Units of Dumlupınar University. Melt tin was heated to 430°C and was atomized at different pressures. Atomization gas was nitrogen. The finest powders have been produced at pressure of 1.47 MPa and mean size was 11.39 μm. Powder, generally had smooth surfaces and spherical shapes. Powders with size greater than 20 μm had cellular surface structures. Powders few satellites formation were observed.
Özet
Bu çalısmada, gaz atomizasyon yöntemi ile metal tozu üretimi için, dairesel yarıklı süpersonik bir nozul tasarımı yapılarak metal tozu üretimi gerçeklestirilmistir. Dumlupınar Gaz Atomizasyon ünitesi’nde gerçeklestirilen çalısmalarda, kalay 430°C’ye kadar asırı ısıtılmıs ve farklı basınçlarda atomize edilmistir. Atomizasyon gazı olarak azot kullanılmıstır. En ince tozlar, 1.47 MPa basınçla üretilmis ve ortalama toz boyutu (d50) 11.39μm olarak ölçülmüstür. Tozlar, genelde düzgün yüzeyli ve küresel sekilli olup, 20 μm’den büyük tozlarda hücresel yüzey yapısı görülmüstür. Tozlarda az miktarda uydulaşma olduğu tespit edilmistir.