Journals / Iğdır Üniversitesi Fen Bilimleri Enstitüsü Dergisi / 2016 / Cilt: 6 - Sayı: 4
Synthesis of Ceramic Particles (Al2O3 and TiB2) in Aluminum Matrix
- Pages
- 75–82
- DOI
- —
Abstract
Al2O3 and TiB2 particles have been successfully synthesized in aluminum matrix with in situ reactionsby hot pressing method. Process parameters; sintering temperatures 900-1000oC, pressure of cold pressing: 7 MPahot pressing: 1 MPa and holding times in furnace 5-10 minutes were selected. Composite microstructures andreinforcement particle numbers-sizes were investigated via SEM and EDS analysis. According to the analysisresults; brittle Al3Ti intermetallic transition phase frequently encountered in the literature could be eliminated.
Özet
Al2O3 ve TiB2 partiküller, sıcak presleme yöntemi sayesinde in situ reaksiyonlarla alüminyum matris içindebaşarıyla sentezlenmişlerdir. İşlem parametreleri; sinterleme sıcaklığı 900-1000oC, soğuk presleme basıncı: 7 MPasıcak presleme basıncı: 1 MPa ve fırında bekletme süresi 5-10 dakika olarak seçilmiştir. Kompozit mikroyapıları vetakviye partikül sayı-boyutları SEM ve EDS analizleri vasıtasıyla belirlenmiştir. Analiz sonuçlarına göre; literatürdesıkça rastlanan gevrek Al3Ti intermetalik geçiş fazı elimine edilebilmiştir.