The Effect of Different Sintering Temperature and Time on Tribological and Mechanical Properties in Non Asbestos Brake Pad Manufacturing

Asbest İçermeyen Fren Balata İmalatında Farklı Sinterleme Sıcaklığı ve Süresinin Tribolojik ve Mekanik Özelliklere Etkisi

Abstract

Automotive brake pads are produced by sintering the combination of many different materials. Brake pads are produced with different parameters in different studies. In this study, tribological and mechanical properties of non- asbestos brake pads produced by sintering at different temperatures and different hours were investigated. The friction coefficient, shear strength, specific wear values, temperature, hardness values, density and SEM / EDS analysis of the brake pads were measured and the effects of different sintering temperatures and sintering time effect were observed. It was found that the increase in sintering temperature and sintering time was positive in terms of friction coefficient, specific wear rate, shear stress values and brake pad temperature values.

Özet

Otomotiv fren balataları birçok farklı malzemenin birleşiminin sinterlenmesi ile üretilmektedir. Baltaların farklı üretim parametreleri ile üretildikleri akademik çalışmalardan görülmektedir. Bu çalışmada, farklı sıcaklıklarda ve farklı sürelerde sinterleme ile imal edilen asbest içermeyen balataların, tribolojik ve mekanik özellikleri araştırılmıştır. Üretilen balataların sürtünme katsayısı, kesme dayanımı, özgül aşınma değerleri, sıcaklığı, sertlik değerleri, yoğunluğu ölçülmüş ve SEM/EDS analizi yapılarak farklı sinterleme sıcaklığı ve sürelerinin etkileri gözlemlenmiştir. Sinterleme sıcaklığı ve süresindeki artışın balata sürtünme katsayısı, özgül aşınma oranı, kesme gerilme değerleri ve balata sıcaklık değerleri açısından olumlu olduğu tespit edilmiştir.