Journals / Iğdır Üniversitesi Fen Bilimleri Enstitüsü Dergisi / 2020 / Cilt: 10 - Sayı: 1
Superconducting magnetic hysteresis behaviors in ABO3-type Perovskites
- Pages
- 171–178
- DOI
- —
Abstract
Superconducting magnetic hysteresis properties of the ABO3-type Perovskites are investigated by the effective field theory. It is found that the core (B) atom of the ABO3 exhibits type II superconducting hysteresis behaviors when it interacts antiferromagnetically with the shell (A and O) atoms. Therefore, the magnetic hysteresis curve of B atoms in the ABO3 has binary coercive field points (lower coercivity; Hc1, and upper coercivity; Hc2). B atoms have a Meissner state at HHc2. Our results indicate that the superconducting properties of the ABO3-type Perovskites result from the antiferromagnetic interaction between the shell (O) and core (B) atoms.,>
Özet
ABO3-tipi perovskitlerin süperiletken manyetik histerezis özellikleri Kaneyoshi tarafından geliştirilen etkin alan teorisi ile incelendi. ABO3’ün merkez atomu (B) kabuk atomları (A ve O) ile antiferromanyetik etkileştiğinde tip II süperiletken davranışı gösteriyor. Böylece, B atomunun manyetik histerezis eğrisi iki zorlayıcı alan noktasına sahip oluyor (düşük zorlayıcı nokta; Hc1 ve yüksek zorlayıcı nokta; Hc2). B atomu HHc2 olduğunda normal durumdadır. Sonuçlarımıza göre ABO3-tipi perovskitlerin süper iletkenlik özellikleri kabuk (O) ve merkez (B) atomlarının antiferromanyetik etkileşmesinin bir sonucudur.ğunda>