Journals / Erciyes Üniversitesi Fen Bilimleri Enstitüsü Fen Bilimleri Dergisi / 2005 / Cilt: 21 - Sayı: 1
DEPENDENCY OF MICROSTRUCTURE PARAMETERS ON THE SOLIDIFICATION PARAMETERS IN THE DIRECTIONALY SOLIDIFIED SUCCINONITRILEACETONE ALLOY
- Pages
- 1–12
- DOI
- —
Abstract
Succinonitrile-3.61wt.% Acetone alloy was unidirectionally solidified with a constant growth rate (V = 6.5 µm/s) at five different temperature gradients (G = 3.53-5.70 K/mm) and with a constant temperature gradient (G = 5.70 K/mm) at five different growth rates (V = 6.5-113.0 µm/s). The primary dendrite arm spacings, secondary dendrite arm spacings, dendrite tip radius and mushy zone depth were measured. The values of microstructure parameters (λ1, λ2, R and d) decrease as the values of solidification parameters (G and V) increase. The obtained results for the microstructure parameters have been compared with the experimental observations, and a comparison of our results with the previous experimental results have also been made.
Özet
Succinonitril-ağ.% 3.61 Aseton organik alaşımı sabit büyütme hızında (V = 6.5 µm/s) beş farklı sıcaklık gradyenti için (G = 3.53-5.70 K/mm) ve sabit sıcaklık gradyentinde (G = 5.70 K/mm) beş farklı büyütme hızı için (V = 6.5- 113.0 µm/s) tek yönlü doğrusal olarak katılaştırılmıştır. Birincil dendrit kol mesafesi, ikincil dendrit kol mesafesi, dendrit uç yarıçapı ve yumuşak bölge derinliği ölçülmüştür. Katılaştırma parametrelerinin (G, V) değerinin artmasıyla mikroyapı parametrelerinin (λ1, λ2, R ve d) değerinin azaldığı gözlenmiştir. Elde edilen mikroyapı parametreleri ile literatürdeki deneysel sonuçlar karşılaştırılmıştır.