AN INVESTIGATION INTO THE MACHINABILITY OF 30MnVS6 MICROALLOYED STEELS BASED ON CUTTING FORCES AND SURFACE ROUGHNESS

SERTLEŞTİRİLMİŞ 30MnVS6 MİKROALAŞIMLI ÇELİĞİN KESME KUVVETLERİ VE YÜZEY PÜRÜZLÜLÜĞÜ AÇISINDAN İŞLENEBİLİRLİĞİNİN ARAŞTIRILMASI

Abstract

In this study, high strength low alloy 30MnVS6 micro alloyed steel workpieces were subjected to hardening heat treatment in oil and water and then machining tests were carried out on them. The machining tests were carried out at four different cutting speeds (90, 120, 150 and 180 m/min), 0.1 mm/rev feed rate and 1 mm depth of cut in dry conditions fluid. The heat treatments applied to the work pieces changed their microstructures and hardness and the effect of different microstructure and hardness on cutting force and surface roughness was investigated. Specimens hardened in water resulted in rapid tool wear. In addition, the water hardened specimen produced higher cutting forces and surface roughness during machining when compared to the oil hardened one.

Özet

Bu çalışmada, yağda ve suda sertleştirme ısıl işlemine tabi tutulan, yüksek dayanımlı düşük alaşımlı (YDDA) 30MnVS6 mikroalaşımlı çelik iş parçaları üzerinde işleme deneyleri yapılmıştır. Deneyler tornalama metoduyla dört farklı kesme hızında (90, 120, 150 ve 180 m/dak) ve 0,1 mm/dev ilerleme miktarı ile 1 mm talaş derinliğinde soğutma sıvısı kullanılmadan kuru şartlarda yapılmıştır. Uygulanan ısıl işlemler iş parçalarının mikroyapılarını ve sertliklerini değiştirmiş ve bu mikroyapıların ve sertliklerin kesme kuvveti ve yüzey pürüzlülüğüne etkileri araştırılmıştır. Suda soğutulan iş parçaları, kesici takımda çok hızlı aşınmaya neden olmuştur. Aynı zamanda, suda sertleştirilen iş parçaları üzerinde yapılan deneylerde kesme kuvvetleri ve yüzey pürüzlülük değerleri yağda sertleştirilen malzemeye göre yüksek bulunmuştur.