The Effect of Fiber Type and Ratio on Physical and Mechanical Properties of Fiber Reinforced Polymer Composite Materials

Lif Takviyeli Polimer Kompozit Malzemelerde Lif Türü ve Oranının Fiziksel ve Mekanik Özelliklere Etkisi

Abstract

In this study, the effect of the types and rations of fiber on the properties of polymer-fiber composite was investigated. The polypropylene, glass, carbon and steel were used as the phase material in the production of polymer concrete. The polymer-fiber composite was prepared using Bisphenol-A epoxy vinylester types of resin and the phase materials at the five different rations (0%-3%-6%-9%-12%). The reaction temperature test, Schmidt surface hardness, ultrasonic pulse velocity, flexural and compressive strength tests were performed on the prepared mixtures and samples. According to the experimental results, the properties examined vary according to the type and proportion of fibers. It has been proposed that the fibers (polymer-fiber composite) should be used for increasing the bending strength.

Özet

Bu çalışmada lif takviye malzemesi oranının, polimer-lif kompozit özellikleri üzerindeki etkisi araştırılmıştır. Polimer beton üretiminde faz malzeme olarak polipropilen, cam, karbon ve çelik lif çeşitleri kullanılmıştır. Bisfenol-A epoksi vinilester reçine ve beş farklı oranda (% 0-3-6-9-12 oranlarında) faz malzemesi olarak kullanılarak polimer-lif kompozit üretimleri gerçekleştirilmiştir. Üretilen numuneler üzerinde reaksiyon sıcaklığı, ultrases geçiş hızı, schmidt çekici ile yüzey sertliği, eğilme ve basınç deneyleri uygulanmıştır. Deneysel sonuçlara göre incelenen özellikler lif tipi ve oranına göre değişkenlik göstermekle birlikte,eğilme mukavemetlerinin arttırılması ve reaksiyon sıcaklıklarından oluşan çatlakların önlenmesi için liflerin polimer-lif kompozit kullanılması önerilmiştir.