Abstract

In this study, borogypsum, an industrial waste, evaluated in the production of diammonium phosphate and boron content fertilizer was investigated. In laboratory conditions 1: 0.25 with diammonium phosphate borogypsum; 1.00:0,25; 1.00:0.50; 1.00:0.75; 1.00:1.00; 1.00:1.25; 1.00:1.50 was used. During mixing, the K / S ratio is 1.5, the temperature is 35 ° C, the mixing time is 60 minutes, the pulp initial mixing pH is 5.5-6.5 and the mixing speed is 600 rpm. The results were as follows: 1.00: 0.25 with diammonium phosphate, borogypsum; 1.00: 0.50; 1.00: 0.75. The possibility of the use of borogypsum as a waste of boric acid production in the production of boron-containing diammonium phosphate has been determined.

Özet

Sunulan çalışmada endüstriyel atık olan borojipsin diamonyum fosfat üretiminde değerlendirilerek bor içerikli gübre elde edilmesi incelenmiştir.. Laboratuvar koşullarında diamonyum fosfat, borojips atığı ile 1,00:0,25; 1,00:0,50; 1,00:0,75; 1,00:1,00; 1,00:1,25; 1,00:1,50 mol oranlarında karıştırılmıştır. Karışma esnasında K/S oranı 1,5, sıcaklık 35°C, karışma süresi 60 dakika, pulpun başlangıç karışma pH’ı 5,5 ve karışma hızı 600 devir/dak. tutuldu. İncelemeler sonucunda diamonyum fosfatın borojips atığı ile 1,00:0,25; 1,00:0,50; 1,00:0,75 oranlarında karıştırılmasının uygun olduğu belirlenmiştir. Sonuç olarak bor içerikli diamonyum fosfat üretiminde, borik asit üretiminin atığı olan borojipsin kullanımı uygun görülmüştür.