Long Term Water Absorption Behaviours of Wood Polymer Nanocomposites Reinforced with Carbon Nanotubes

Karbon Nanotüp İle Güçlendirilen Ahşap Polimer Nanokompozitlerin Uzun Süreli Su Alma Davranışlarının Belirlenmesi

Abstract

The water absorption of wood polymer nanocomposites prepared from polypropylene/pine wood flour, carbon nanotube and coupling agent was studied. The pine wood flour, carbon nanotube and MAPP were compounded in a twin screw co-rotating extruder. Test specimens were produced by injection molding process from the pellets dried to moisture content of 1%. Long term water absorptions of manufactured nanocomposites were evaluated by immersing them in water at room temperature for several weeks (for 6 months). Results indicated that water absorption and thickness swelling properties increased with increasing carbon nanotube content. Also adding the MAPP improved the dimensional stability properties of the nanocomposites.

Özet

Bu çalışmada polipropilen, çam ahşap unu ve karbon nanotüp kullanılarak üretilen ahşap polimer nanokompozitlerin su alma davranışı incelenmiştir. Bu amaç doğrultusunda çam ahşap unu, Polipropilen, karbon nanotüp ve uyum sağlayıcı ajan çift vidalı ekstruder içerisinde homojen bir biçimde karıştırılmıştır. Daha sonra elde edilen peletler enjeksiyon kalıplama makinesi kullanılarak fiziksel özelliklerin tespitinde kullanılan numunelerin üretimi sağlanmıştır. Ahşap polimer nanokompozitlerin uzun sureli su alma davranışı 6 ay boyunca takip edilmiştir. Elde edilen sonuçlar karbon nanotüp kullanımının ahşap polimer nanokompozitlerin fiziksel özelliklerini iyileştirdiğini göstermiştir. Ayrıca uyum sağlayıcı ajan (MAPP) kullanımının ahşap polimer nanokompozitlerin boyutsal stabilizasyonunu arttırdığı görülmüştür.