The Improvement of Magnetic Levitation and Guidance Force of SiC added to MgB2 Bulk Samples
- Pages
- 595–601
- DOI
- —
Abstract
The effect of SiC from 0 to 25 wt% of the total MgB2 addition on the magnetic levitation force and guidance lateral force properties of bulk MgB2 superconductor has been investigated. The amount of SiC was varied between 0 and 25 wt% of the total of MgB2 . The vertical levitation force measurements were carried out under zero-field-cooled ZFC and field-cooled FC regimes at 20 K. Lateral guidance force measurements were carried out under FC regime at 25 K. The structural and electrical properties of samples were investigated with X-ray diffraction XRD and low temperature resistance measurement. It was obtained that 5 wt%, 10 wt%, 15 wt% and 20 wt% SiC added samples exhibit a higher levitation and guidance forces than püre sample. It was found that that10 wt% SiC adding sample has the best magnetic levitation and guidance force performances
Özet
Bu çalışmada Katıhal Tepkime yöntemiyle üretilen silindirik külçe MgB2 süperiletken örneklerine SiC eklenmesinin manyetik kaldırma ve kılavuzlama kuvvetleri üzerine etkisi araştırıldı. SiC miktarı, toplam MgB2’nin ağırlıkça %0, %5, %10, %15, % 20 ve %25 olarak seçildi. Manyetik kaldırma kuvveti ölçümleri sıfır alan altında soğutma ZFC ve alan altında soğutma FC rejimleri altında, 20 K sıcaklığında; kılavuzlayıcı yanal kuvvet ölçümü ise FC rejiminde, 25 K sıcaklığında gerçekleştirildi. Örneklerin yapısal ve elektriksel özellikleri X-ışını kırınımı XRD ve düşük sıcaklık direnç ölçümü ile incelendi. %5, %10, %15 ve %20 SiC eklenmiş örneklerde, saf MgB2 örneğine kıyasla daha büyük manyetik kaldırma ve yanal manyetik kılavuzlama kuvvet değerleri elde edildi. Tüm örnekler içerisinde en büyük manyetik kaldırma ve yanal manyetik kuvvet %10 SiC eklenmiş MgB2 örneğine ait olduğu bulundu