Certain physical and mechanical properties of medium density fiberboards manufactured from blends of corn (Zea mays indurata Sturt.) stalks and pine (Pinus nigra) wood
- Pages
- 197–206
- DOI
- —
Abstract
Corn stalk is a renewable natural resource that currently has limited industrial utilization. The objective of this study was to examine some chemical properties of corn stalk (holocellulose, a-cellulose, lignin and ash content, alcohol-benzene, hot and cold water solubility, and solubility in dilute alkali [1% NaOH]) and to evaluate its suitability for medium-density fiberboard (MDF) production. Panels were produced using mixtures of corn stalk (Zea mays indurata Sturt.) and pine (Turkish Pinus nigra) fibers in various proportions (from 0% to 100%). The panels produced had density levels of 0.6, 0.7, and 0.8 g cm-3. The physical and mechanical properties of the manufactured panels were tested. Chemical analysis shows that the holocellulose, a-cellulose, and lignin content of corn stalk was similar to that of wood and some other crop residues. The ash content of corn stalk was higher than that of soft- and hardwoods. Mechanical test results indicate that the panels produced utilizing solely corn stalk met the required standards, except the panels with a density of 0.6 g cm-3. Increasing the pine fiber ratio in the panel mixture improved panel properties.
Özet
Corn stalk is a renewable natural resource that currently has limited industrial utilization. The objective of this study was to examine some chemical properties of corn stalk (holocellulose, a-cellulose, lignin and ash content, alcohol-benzene, hot and cold water solubility, and solubility in dilute alkali [1% NaOH]) and to evaluate its suitability for medium-density fiberboard (MDF) production. Panels were produced using mixtures of corn stalk (Zea mays indurata Sturt.) and pine (Turkish Pinus nigra) fibers in various proportions (from 0% to 100%). The panels produced had density levels of 0.6, 0.7, and 0.8 g cm-3. The physical and mechanical properties of the manufactured panels were tested. Chemical analysis shows that the holocellulose, a-cellulose, and lignin content of corn stalk was similar to that of wood and some other crop residues. The ash content of corn stalk was higher than that of soft- and hardwoods. Mechanical test results indicate that the panels produced utilizing solely corn stalk met the required standards, except the panels with a density of 0.6 g cm-3. Increasing the pine fiber ratio in the panel mixture improved panel properties.