Journals / Düzce Üniversitesi Orman Fakültesi Ormancılık Dergisi / 2013 / Cilt: 9 - Sayı: 1
Analysis of Fiber Morphological and Chemical Properties of European Aspen (populus tremula L.) growing naturally in Turkey
- Pages
- 55–61
- DOI
- —
Abstract
In this study, chemical analysis and fiber structure of aspen (Populus tremula L.) tree were analyzed. The log of Aspen tree was obtained from Arit chief in Bartin forest management. Ratios of main chemical components of aspen tree, holocellulose, cellulose, lignin and ash content, hot and cold water solubility, % 1 NaOH and alcohol-benzene solubility, respectively. As a result, holocellulose, cellulose, lignin, ash content, the resolution of hot and cold water, %1 NaOH and respectively, alcohol-benzene resolution, %85.7, %58, %17.2, %0.28, %14,9, %5.86 and %19.2, respectively.In addition, measurements of fiber, fiber length, vessel size, lumen width, double wall thickness, elasticity ratio, Runkel classification rate and rigidity values were felting 1.33 mm, 695.1 μm, 22.6 μm, 17.1 μm, 10.4 μm, % 53.5, 0.86, %58.9 and 20.1 respectively. These results obtained here are by and large parallel to those of previous studies aspen tree species.
Özet
Bu çalışmada titrek kavak (Populus tremula L.) ağacının kimyasal analizleri ve lif yapısı incelenmiştir. Titrek kavak odunu, Bartın orman işletme müdürlüğüne bağlı Arıt şefliğinden temin edilmiştir. Yapılan çalışmalar ile titrek kavak ağacının holoselüloz, selüloz, lignin ve kül oranı bileşenleri ile, sıcak ve soğuk su, %1 NaOH ve Alkol-Benzen çözünürlüğü % olarak belirlenmiştir. Sonuç olarak holoselüloz, selüloz, lignin, kül, sıcak ve soğuk su da çözünürlük, %1 NaOH ve Alkol-Benzen çözünürlüğü sırası ile %85.7, %58, %17.2, %0.28, %14,9, %5.8 ve %19.2 olarak tespit edilmiştir.