Corrosion Effects on Fatigue Behavior of Zn-Cr+3 and Zn Flake Coated M8 DIN 933 Bolts

Sezgin YURTDAŞ
Umut İNCE
Barış TANRIKULU
Cenk KILIÇASLAN
Muhammed Burak TOPARLI
Pages
867–874
Publication Date
2021-08-30
DOI
—
🏛️Bibliographic metadata and full text access for this article are provided via DergiPark.
DergiPark Record ↗
✨

AI Summary & Key Takeaways

AI Insight
⚡ TL;DR(Too Long; Didn't Read)

For both coatings and corrosion conditions, fatigue cracks were seen to initiate from the thread roots.

📌 3 Key Takeaways

🎯
Objective & Hypothesis:In this study, fatigue behavior of Zn-Cr+3 and zinc flake coated bolts was investigated experimentally by considering corrosion effects.
📊
Key Findings & Data:Fatigue tests were conducted on M8x50x1.25 8.8 DIN 933 bolts at normal and corroded conditions at force amplitudes between 2.35 and 5.36 kN at test frequency of 75 Hz.
💡
Conclusion & Impact:For both coatings and corrosion conditions, fatigue cracks were seen to initiate from the thread roots.
🔬Design:Research Article
📍Scope:Comprehensive Sample
⚙️Variables:Bolt · fatigue life · coating

Abstract

In this study, fatigue behavior of Zn-Cr+3 and zinc flake coated bolts was investigated experimentally by considering corrosion effects. Fatigue tests were conducted on M8x50x1.25 8.8 DIN 933 bolts at normal and corroded conditions at force amplitudes between 2.35 and 5.36 kN at test frequency of 75 Hz. A part of bolts was subjected to salt atmosphere for corrosion. According to the Wöhler curves obtained from fatigue tests before corrosion, zinc flake coated bolts showed 1.55 times higher fatigue life compared to Zn-Cr+3. After corrosion, fatigue tests showed that the fatigue life difference increased to 2.10 times for the zinc flake coating. Moreover, corrosion was found to be ineffective on crack initiation region. For both coatings and corrosion conditions, fatigue cracks were seen to initiate from the thread roots.

🔖

Cite This Article

YURTDAŞ, S., İNCE, U., TANRIKULU, B., KILIÇASLAN, C., TOPARLI, M. B. (2021). Corrosion Effects on Fatigue Behavior of Zn-Cr+3 and Zn Flake Coated M8 DIN 933 Bolts. Sakarya University Journal of Science, Cilt: 25 Sayı: 4, 867–874. https://ajindex.com/articles/941768

📄 Full Text PDF Viewer

📄

PDF görüntüleyici hazırlanıyor...

References (13)

  1. M. Metallurgy vd., “Elements of Metallurgy and Engineering Alloys”, Elem. Metall. Eng. Alloy., 2019, doi: 10.31399/asm.tb.emea.9781627082518
  2. A. Hudgins ve B. James, “Fatigue of threaded fasteners”, Adv. Mater. Process., c. 172, sayı 8, ss. 18–22, 2014
  3. P. Zampieri, A. Curtarello, C. Pellegrino, ve E. Maiorana, “Fatigue strength of corroded bolted connection”, Frat. ed Integrita Strutt., c. 12, sayı 43, ss. 90–96, 2018, doi: 10.3221/IGF-ESIS.43.06
  4. L. Mordfin, “Some Problems of Fatigue of Bolts and Bolted Joints in Aircraft Applications”, U. S. Dep. Commer. Natl. Bur. Stand., 1962
  5. S. Ifergane vd., “The effect of manufacturing processes on the fatique lifetime of aeronautical bolts”, Eng. Fail. Anal., c. 8, sayı 3, ss. 227–235, 2001, doi: 10.1016/S1350-6307(00)00013-3
  6. A. L. Marcelo, A. Y. Uehara, R. M. Utiyama, ve I. Ferreira, “Fatigue properties of high strength bolts”, Procedia Eng., c. 10, ss. 1297–1302, 2011, doi: 10.1016/j.proeng.2011.04.216
  7. M. N. A. S. Shuhaib, “Experimental Evaluation of the Effect of Thread Angle on the Fatigue Life of Bolts”, Int. J. Fatigue, c. 7, sayı 1, ss. 12–19, doi: 10.1016/j.ijfatigue.2004.06.011
  8. G. H. Majzoobi, G. H. Farrahi, ve N. Habibi, “Experimental evaluation of the effect of thread pitch on fatigue life of bolts”, Int. J. Fatigue, c. 27, sayı 2, ss. 189–196, 2005, doi: 10.1016/j.ijfatigue.2004.06.011
  9. S. Griza, M. E. G. da Silva, S. V. dos Santos, E. Pizzio, ve T. R. Strohaecker, “The effect of bolt length in the fatigue strength of M24×3 bolt studs”, Eng. Fail. Anal., c. 34, ss. 397–406, Ara. 2013, doi: 10.1016/j.engfailanal.2013.09.010
  10. E. A. P. J.W. Hobbs, R.L. Burguete, P.F. Heyes, “The effect of eccentric loading on the fatigue performance of high-tensile bolts”, Int. J. Fatigue, c. 22, sayı 6, ss. 531–538, Tem. 2000, doi: 10.1016/S0142-1123(00)00004-9
  11. L. Solazzi, R. Scalmana, M. Gelfi, ve G. M. L. Vecchia, “Effect of different corrosion levels on the mechanical behavior and failure of threaded elements”, J. Fail. Anal. Prev., c. 12, sayı 5, ss. 541–549, 2012, doi: 10.1007/s11668-012-9593-x
  12. H. L. Wang, J. G. Xia, ve S. F. Qin, “High-strength bolt corrosion fatigue life estimate model and its application”, Dalian Haishi Daxue Xuebao/Journal Dalian Marit. Univ., c. 40, sayı 3, 2014
  13. N. Sanaei ve A. Fatemi, “Analysis of the effect of surface roughness on fatigue performance of powder bed fusion additive manufactured metals”, Theor. Appl. Fract. Mech., c.