AI InsightIn addition, 80 percent of concrete containing blast furnace slag resistances to seawater were higher than the control sample
📌 3 Key Takeaways
Abstract
In this study, ground granulated blast furnace slag and basalt together or separately using pumice abrasion resistance power of the concrete produced was investigated. In different proportions of fine aggregate instead of blast furnace slag or basalt samples were produced using pumice. Three years are exposed to sea water corrosion mass loss of the samples was determined according to. Blast furnace slag and basalt pumice for specimens which had a positive effect against abrasion were found. Concrete durability, depend on the type and amount of additives has been shown. In addition, 80 percent of concrete containing blast furnace slag resistances to seawater were higher than the control sample
Özet
Bu çalışmada, öğütülmüş yüksek fırın cürufu ve bazaltik pomza ayrı ayrı veya birlikte kullanılarak üretilen betonların hidrolik aşınmaya dayanıklılığı araştırılmıştır. İnce agreganın yerine değişik oranlarda yüksek fırın cürufu veya bazaltik pomza kullanılarak numuneler üretilmiştir. Üç yıl deniz suyu etkisine maruz kalan örneklerin aşınmaları kütle kayıplarına göre belirlenmiştir. Yüksek fırın cürufu ve bazaltik pomza katkılı numunelerin aşınmaya karşı olumlu etkiler yaptığı görülmüştür. Beton dayanıklılığının, katkı tipi ve miktarına bağlı olduğu ortaya konmuştur. Ayrıca yüzde 80 yüksek fırın cürufu içeren betonların deniz suyuna karşı dayanıklılığı kontrol numunesinden daha yüksek bulunmuştur